Ripple structure of ion beam induced Si wafer — •Ullrich Pietsch1, J. Grenzer1, S. Hazra2, T.K. Chini2, and M.K. Sanyal2 — 1University of Potsdam, Institute of Physics, 14415 Potsdam, Germany — 2Surface Physics Division, Saha Institute of Nuclear Physics, 1/AF Bidhannagar, Kolkata 700 064, India
Ion beam induced ripple formation in Si wafers was studied by atomic force microscopy (AFM) and non-destructive depth-resolved x-ray grazing incidence diffraction (GID). The formation of ripple structure at high doses (7x10 17 ions/cm2), starting from initiation at low doses (1x10 17 ions/cm2) of ion beam is evident from AFM, while that in the buried crystalline region below a partially crystalline top layer is evident from GID study. The GID technique reveals that these periodically modulated wave-like buried crystalline features become highly regular and strongly correlated as one increases the Ar ion beam energy from 60 keV to 100 keV. The vertical density profile obtained from the analysis of Vineyard profile shows that the density in the upper top part of ripples is decreased to about 15% of the crystalline density. The partially crystalline top layer at low dose, transforms to a completely amorphous layer for high doses and the top morphology was found to be conformal with the underlying crystalline ripple. On the other hand, the amorphous part of the damaged top layer is textured and scales with the ion dose. S. Hazra, T.K. Chini, M.K. Sanyal, J. Grenzer and U. Pietsch, Phys.Rev.B70 121307(R) 2004