MA 20.19: Poster
Monday, March 7, 2005, 14:00–18:00, Poster TU C
Observation of the Fe Spin Spiral Structure in Fe/Sm-Co Exchange Spring Bilayers by 57Fe-Probe Layer Mössbauer Spectroscopy — •A. Khrenov1, W. Keune1, V.E. Kuncser2, J.S. Jiang3 und S.D. Bader3 — 1Angewandte Physik, Universität Duisburg-Essen, 47048 Duisburg — 2NIPM, RO-76900 Bucharest Magurele, Romania — 3Materials Science Div., Argonne National Laboratory, Argonne, IL 60439, USA
The layer resolved Fe spin spiral structure for Fe/Sm-Co(1100)
exchange spring magnetic bilayers was investigated by 57Fe conversion
electron Mössbauer spectroscopy (CEMS) during the magnetization reversal
process, and correlated with the hysteresis loops measured via the
magneto-optic Kerr effect. 2 nm thick isotopically enriched 57Fe-probe
layers were sputter-deposited in the 20 nm thick natural Fe layer at
different distances from the Fe/Sm-Co interface. A direct experimental
proof for a relaxed spiral angular spin distribution in the Fe layer is
presented. Contrary to expectation, weak out-of-plane Fe spin components
were observed in a certain applied field range.
Sponsored through Deutsche Forschungsgemeinschaft (SFB491) and DOE Contract
No. W.31-109-ENG-38.