Effect of Equal Channel Angular Pressing on the Deformation Behaviour of Magnesium Alloy AZ31 under Uniaxial Compression — •Zuzana Zúberová1, Yuri Estrin1, Torbjørn T. Lamark1, Miloš Janeček2, Ralph J. Hellmig1, and Markus G. Krieger1 — 1Institut für Werkstoffkunde und Werkstofftechnik, Technische Universität Clausthal, Agricolastr. 6, 38678 Clausthal–Zellerfeld — 2Charles University, Faculty of Mathematics and Physics, Ke Karlovou 5, 12116 Prague 2, Czech Republic
The deformation behaviour of the magnesium alloy AZ31 under uniaxial compression was investigated using specimens produced by squeeze casting, hot rolling and hot rolling with subsequent equal channel angular pressing (ECAP). ECAP was performed up to 4 passes at 200∘C following route BC leading to a homogeneous fine–grained microstructure and improved mechanical properties. Results of compression tests under various testing conditions as well as microstructural investigations are presented and discussed.