10keV He ion bombardment of Ni80Fe20/Au/Co/Au multilayers with alternating in-plane and out-of-plane magnetization — •Tanja Weis1, Dieter Engel1, Arno Ehresmann1, Maria Tekielak2, Andrzej Maziewski2, Bogdan Szymanski3, Janusz Dubowik3, and Feliks Stobiecki3 — 1Institute of Physics and CINSaT, University of Kassel, Heinrich-Plett-Str. 40, 34132 Kassel, Germany — 2Institute of Molecular Physics, Polish Academy of Sciences, ul. Smoluchowskiego 17, 60-179 Poznan, Poland — 3Institute of Experimental Physics, University of Bialystok, Lipowa 41, 15-424 Poland
Ion bombardment with light ions enables the alteration of the magnetic properties in magnetic thin film systems [1]. This technique was used to modify magnetic anisotropies in Ni80Fe20/Au/Co/Au multilayers. The as-prepared multilayers show prior to bombardment alternating in-plane (NiFe) and out-of-plane (Co) magnetization. We will present Kerr Microscopy images of 10keV He ion bombarded samples with either Au- or Co-wedges to show the dependence of the modifications of magnetic properties like anisotropy and interlayer coupling on the Au- and Co- thickness (tAu and tCo) and on the ion dose. Due to an increase of interface roughness the surface induced perpendicular anisotropy is reduced for 0.95nm ≤ tCo ≤ 1.05nm. On the other hand the ion bombardment heavily mixes ultrathin Co layers (0.35nm ≤ tCo ≤ nm) resulting in their superparamagnetic behavior.