O 42: Poster Session II (Nanostructures at surfaces: arrays; Nanostructures at surfaces: Dots, particles, clusters; Nanostructures at surfaces: Other; Nanostructures at surfaces: Wires, tubes; Metal substrates: Adsorption of O and/or H; Metal substrates: Clean surfaces; Metal substrates: Adsorption of organic/bio moledules; Metal substrates: Solid-liquid interfaces; Metal substrates: Adsorption of inorganic molecules; Metal substrates: Epitaxy and growth; Heterogeneous catalysis; Surface chemical reactions; Ab-initio approaches to excitations in condensed matter; Organic, polymeric, biomolecular films– also with adsorbates; Particles and clusters)
O 42.18: Poster
Mittwoch, 25. März 2009, 17:45–20:30, P2
Klusterexperimente an dünnen Co-PLD-Schichten und Schichtsystemen — Markus Trautmann, Rober Hähle, Janine Fischer, Ingo Sill, Andre Bikowski, Thomas Schmidt, Veit Grosse, •Frank Schmidl und Paul Seidel — FSU Jena, Institut für Festkörperphysik, Helmholtzweg 5, 07743 Jena, Germany
Für das gezielte Wachstum von Kohlenstoffnanoröhren (CNT’s)spielen ferromagnetische Kluster (Co,Fe,Cr) eine entscheidende Rolle. Wir stellen Untersuchungen zur strukturierten Abscheidung von dünen Co-Schichten mittels lasergestützter Abscheidung (PLD) vor. Es wurden Klusterexperimente auf Si-Substraten mit und ohne SiO2- Einzelschichten bzw. Schichtsystemen durchgeführt. Wir diskutieren die Messungen zur Klustergröße in Abhängigkeit von Ausgangsschichtdicke, Klustertemperatur und Substratmaterial im Hinblick auf eine mögliche in-situ Abscheidung von CNT’s mittels PLD.