Surface structure and electronic properties of epitaxial off-stoichiometric Ni-Mn-Ga films — •Aleksej Laptev1, Philipp Leicht1, Mikhail Fonin1, Yuansu Luo2, Konrad Samwer2, Yuriy Dedkov3, and Martin Weser3 — 1Fachbereich Physik, Universität Konstanz, 78457 Konstanz — 2I. Physikalisches Institut, Georg-August-Universität Göttingen, 37077 Göttingen — 3Fritz-Haber-Institut der Max-Planck-Gesellschaft, 14195 Berlin
Ni2MnGa alloys have attracted considerable interest due to the large magnetic field-induced strain and their possible applications as microscale actuators or sensors. Upon cooling from the austenite phase a transformation to the martensite phase occurs for these materials. Here we report on the investigation of epitaxial off-stoichiometric Ni-Mn-Ga films grown on MgO substrates by dc-magnetron sputtering. To achieve appropriate surface quality the samples were treated under ultra high vacuum conditions by repeated cycles of sputtering and annealing. The crystal structure changes at the Ni-Mn-Ga (100) surface during the reversible phase transition were followed by LEED. A splitting of the main reflexes due to a longer range ordering of the surface was observed upon cooling. The twin boundary formation together with the modulation of the structure was imaged by high resolution STM in the martensite phase. Electronic properties were investigated by ultra-violet photoemission spectroscopy showing pronounced differences in the valence band spectra of two phases. Financial support by the BMBF within MSM-Sens 13N10061 and 13N10062 is gratefully acknowledged.
This document was translated from LATEX by HEVEA.