Pore lattice deformation of silica nanochannels (SBA-15) during uptake and release of solid and liquid argon — •Daniel Rau1, Dirk Wallacher2, Gerald Zickler3, Patrick Huber1, and Rolf Pelster11FR 7.2 Experimentalphysik, Universität des Saarlandes, Germany — 2Helmholtz Zentrum Berlin, Germany — 3Department of Physical Metallurgy and Materials Testing, Montanuniversität / University of Leoben, Austria

We have studied the structural change of cylindrical, hexagonally ordered silica nanopores (SBA-15) as a function of their filling with solid and liquid argon, respectively. Sorption isotherms were measured at 71.5 K (solid) and 81.5 K (liquid). Simultaneously the material was characterized via small-angle-X-ray-scattering (SAXS) using synchrotron radiation at the Hasylab (DESY/Hamburg). In this way we are able to evaluate the deformation of the pore lattice during adsorption and desorption.

100% | Mobile Layout | Deutsche Version | Contact/Imprint/Privacy
DPG-Physik > DPG-Verhandlungen > 2011 > Dresden