High-pressure synthesis of 1111-pnictides and related systems — •Agnes Adamski1, Amir Haghighirad1,2, Steffi Hartmann1, Natalija van Well1, and Cornelius Krellner1 — 1Physikalisches Institut, Goethe University, Frankfurt am Main, — 2University of Oxford, Department of Physics, Oxford
In 2008 Kamihara et al. found a new class of high-Tc superconductors: iron-based oxypnictides. A transition temperature of 26 K in F-doped LaFeAsO (1111-compound) was reported [1]. Replacing the nonmagnetic La ion by magnetic rare-earth elements in 1111-compounds leads to an increase of the superconducting transition temperatur up to ~50 K. The crystal growth at high pressure/high temperature (HP/HT) conditions has been proven to be an effective method for the 1111-compounds [2][3].
We report on our progress to synthesize single crystals of these compounds under HP/HT conditions with a multi anvil apparatus, so called Walker-Type module. With this apparatus we can achieve rather hydrostatic pressures up to 8 GPa and temperatures up to 1750 K. We found that using NaCl/KCl as flux material is essential to avoid the formation of FeAs and to support the single crystal growth. The same Walker-Type module was used for the synthesis of related pnictides to search for new superconductors. It seems that high pressure is necessary to stabilized these compounds.