Ferromagnetism of nonstoichiometric manganese monosilicides at room temperature — •Anna S. Semisalova1,2, Konstantin Yu. Chernoglazov3, Nikolai S. Perov1, Elena A. Gan'shina1, Alexander B. Granovsky1, Andrey V. Zenkevich4, Shengqiang Zhou2, and Vladimir V. Rylkov3 — 1Lomonosov MSU, Moscow, Russia — 2HZDR, Dresden, Germany — 3NRC Kurchatov Institute, Moscow, Russia — 4MIPT, Dolgoprudny, Russia
Ferromagnetic Si-Mn alloys attract increasing interest due to their interesting properties - recently it was found that these alloys prepared by PLD method exhibit unusual magnetic characteristics which cannot be adequately interpreted within the framework of available theoretical models. Curie temperature TC in nonstoichiometric Si1-xMnx alloys slightly enriched in Mn (x ~ 0.52-0.55) was shown to be on order of magnitude higher (TC ~ 300 K) in comparison to the stoichiometric MnSi (TC ~ 30 K). The mechanism of high-temperature ferromagnetism is still not clear. The ferromagnetic exchange is associated with the formation of defects with localized magnetic moments coupled via spin fluctuations of itinerant electrons in the host. Also we suppose that structural defects have a strong influence on the formation of metastable phases with enhanced ferromagnetic response. In this contribution the recent experimental results on ferromagnetosm of PLD deposited SiMn alloys are summarized. Supported by RFBR (15-57-78022). 1. Rylkov et al. EPL 103, 57014 (2013) 2. Rylkov et al. JMMM, doi:10.1016/j.jmmm.2014.09.028