Epitaxial growth and characterization of Mn2Au thin films for antiferromagnetic spintronics — •Helge Bräuning, Mathias Kläui, and Martin Jourdan — Institut für Physik, Johannes Gutenberg Universität, Staudingerweg 7, 55128 Mainz, Germany
The antiferromagnetic compound Mn2Au is characterized by large spin-orbit coupling, which makes it a promising material for novel antiferromagnetic spintronics (see e.g. [Bar13, Zel14]).
We prepared thin films of Mn2Au by RF-sputtering from a stoichiometric target on MgO and Al2O3 substrates using different buffer layers. Epitaxial samples with different growth directions such as [100], [001], and [101], were obtained. The samples were characterized by x-ray diffraction, magnetometry, AFM and SEM. Additionally, magnetotransport investigations will be presented.
[Bar13] V.M.T.S. Barthem et al. Nat. Commun. 4, 2892 (2013).
[Zel14] J. Zelezny et al. Phys. Rev. Lett. 113, 157201 (2014).