Ferroelasticity in methylammonium lead halide perovskite? — •Ilka Hermes1, Simon Bretschneider1, Victor Bergmann1, Dan Li1, Alexander Klasen1,2, Julian Mars1, Wolfgang Tremel2, Frédéric Laquai1, Hans-Jürgen Butt1, Markus Mezger1,2, Rüdiger Berger1, Brian Rodriguez3, and Stefan Weber1,21MPI for Polymer Research, Mainz — 2Johannes Gutenberg University, Mainz — 3University College Dublin, Ireland

Methylammonium lead halide (MAPbX3) perovskite materials show an outstanding performance in photovoltaic devices. However, some material properties, especially the possible ferroic behavior, remain unclear. We observed distinct nanoscale periodic domains in the piezoresponse of MAPbI3(Cl) grains. The structure and the orientation of these striped domains is indicating ferroelasticity as their origin. By correlating vertical and lateral piezoresponse force microscopy experiments performed at different sample orientations with x-ray diffraction, the preferred domain orientation was assigned to the a1a2-phase. The observation of the twin domains appears to strongly depend on the preparation route and the film texture and is thought be induced by internal strain during the cubic-tetragonal phase transition.

100% | Mobil-Ansicht | English Version | Kontakt/Impressum/Datenschutz
DPG-Physik > DPG-Verhandlungen > 2016 > Regensburg