Energy Levels at Perovskite/Electron Transport Layer Interfaces — •Fengshuo Zu¹, Johannes Frisch¹, Liangsheng Liao², and Norbert Koch¹ — ¹Institut für Physik & IRIS Adlershof, Humboldt-Universität zu Berlin, Brook-Taylor-Str. 6, 12489 Berlin, Germany — ²FUNSOM,Soochow University, Jiangsu 215123, China

organometal halide perovskites attract substantial attention for high-efficiency thin film solar cells. Numerous studies are focused on film processing and device configuration variation in order to further improve device efficiency, but the fundamental physics in particular regarding interfacial energy level alignment with charge transport materials (e.g., fullerene derivatives) are yet poorly understood. It is generally believed that perovskites form type-II p-n junctions with C60 or PCBM, which would favor the charge separation process at the interface. To substantiate this proposition, we performed TRPL and UPS measurements to investigate the interface energy levels and the charge separation process at perovskite/fullerene junctions. However, contrary to the common believe, our measurements show that both junctions exhibit n-n type-I level alignment. TRPL results show no different decay channels with or without fullerene layers, which indicates the perovskite/fullerene interface does not provide a driving force for charge separation. Nonetheless, our solar cells with PCBM junctions show reasonable performance, with a power conversion efficiency of 9.30%. In constrast, the perovskite/C60 solar cells show much lower efficiency, which we attribute to upward band bending within perovskite when in contact with C60.