MM 17: Nanomaterials

MM 17.10: Vortrag

Dienstag, 2. April 2019, 12:45–13:00, H46

static friction vs young's modulus: the essential factors in reusable anodic aluminum oxide (AAO) template as a master mold — •Huanming Zhang, Min Zhou, Yang Xu, Rui Xu, Zhiqiang Zeng, and Yong Lei — Institute für Physics & IMN MacroNano (ZIK), Technische Universität Ilmenau, 98693 Ilmenau

To construct ordered nanostructure over a large area, Anodic Aluminum Oxide (AAO) template-directed fabrication is a promising technology. Herein, we propose a facial method to fabricate highly ordered metal film with AAO template as a master mold. After metal deposition in the AAO pores, the ordered metal films can be easily obtained by mechanical stripping from AAO template. To obtain a complete metal film, control experiments were conducted, and the aspect of the pore in AAO template and the Young's modulus of the metal deposited in the AAO pores was supposed to be the essential factors. The aspect-dependent static friction interacts with Young's modulus of the metal deposited in the AAO pores closely.