Interaction of polyamide 6 with galvanised steel and the influence of surface pretreatments — •Philipp Moritz1,2, Lisa Wurlitzer1,2, Maria Sonnenberg1,2, and Wolfgang Maus-Friedrichs1,2 — 1Institute of Energy Research and Physical Technologies, Clausthal University of Technology, Leibnizstr. 4, 38678 Clausthal-Zellerfeld — 2Clausthal Centre of Material Technology, Clausthal University of Technology, Agricolastr. 2, 38678 Clausthal-Zellerfeld
Nowadays polymer-metal composites play a key role in the automotive and aerospace industry. The use of lightweight sandwich structures, for example, could lead to lower fuel consumption and decreasing CO2 emissions. In order to improve the mechanical properties of these composites, the physical interaction of the layers is of particular interest.
We have produced composite materials from galvanised steel and polyamide 6 to investigate the bonding in more detail. In order to improve adhesion, the steel surface was additionally coated with a SiOx layer using plasma-enhanced chemical solution deposition (PECSD). In further experiments, the effect of plasma-treated surfaces on the adhesion was investigated.
The adhesion behaviour was characterised by T-Peel tests and the exposed interfaces were studied with electron spectroscopy and microscopy. The spectroscopic analysis indicates different chemical bonds, due to the presence of the SiOx layer.