Magnetostructural phase transition in Fe60V40 alloy thin films — •Md. Shadab Anwar1,3, H. cansever1, B. Boehm2, R. A. Gallardo5, R. Hübner1, S. Zhou1, U. Kentsch1, B. Eggert4, H. Wende4, K. Potzger1, J. Faßbender1, K. Lenz1, J. Lindner1, O. Hellwig1,2, and R. Bali11Helmholtz-Zentrum Dresden-Rossendorf, Germany — 2TU Chemnitz, Germany — 3TU Dresden, Germany — 4University of Duisburg-Essen, Germany — 5Universidad Técnica Federico Santa María, Chile

Ferromagnetism can be induced in non-ferromagnetic precursors such as B2 Fe60Al40[1] and B2 Fe50Rh50[2] through lattice disordering. Here we study a magnetostructural transition in Fe60V40 thin films using ion-irradiation. We show that the as-grown films possess an Ms of 17 kA/m and irradiation with 25 keV Ne+-ions at a fluence of ∼ 5 x 1015ions/cm2 leads to an increase of Ms to ∼ 750 kA/m. A structural short-range order in the as-grown films can be observed, that transforms to A2 phase (bcc) via ion-irradiation. The A2 region appears to nucleate at the film surface, and with increasing Ne+-fluence, it propagates deeper into the film. Mössbauer spectroscopy and ferromagnetic resonance have been applied to track the variation of local magnetic ordering and dynamic behaviour respectively.

Financial support by DFG grants BA 5656/1-2 and WE 2623/14-2 is acknowledged.

[1]Ehrler, J.et al., New J. Phys.,22,073004(2020)

[2]Eggert, B.et al., RSC Adv.,10,14386(2020)

100% | Mobile Layout | Deutsche Version | Contact/Imprint/Privacy
DPG-Physik > DPG-Verhandlungen > 2021 > SKM