MA 37.1: Talk
Thursday, March 30, 2023, 09:30–09:45, HSZ 403
Enhanced magnetism of antiphase boundaries in Fe2CoAl compound — Martin Friák1, Josef Gracias2, Jana Pavlů2, and •Mojmír Šob2,1 — 1Inst. Phys. Mat., Czech Acad. Sci., Brno, Czech Rep. — 2Dept. Chem., Fac. Sci., Masaryk Univ., Brno, Czech Rep.
We performed a quantum mechanical examination of thermodynamic, structural, elastic, and magnetic properties of single-phase ferromagnetic Fe2CoAl with a chemically disordered B2-type lattice with and without antiphase boundaries (APBs) with (001) crystallographic orientation. Fe2CoAl was modeled using two different 54-atom supercells with atoms on the two B2 sublattices distributed according to the special quasi-random structure (SQS) concept. Both computational models used exhibited very similar formation energies (−0.243 and −0.244 eV/atom), B2-structure lattice parameters (2.849 and 2.850 Å), magnetic moments (1.266 and 1.274 µB/atom), practically identical single-crystal elastic constants (C11 = 245 GPa, C12 = 141 GPa, and C44 = 132 GPa) and auxetic properties (the lowest Poisson ratio close to -0.1). In contrast to these similarities, the averaged APB interface energies were observed to be 199 and 310 mJ/m2 for the two models. The studied APBs increased the total magnetic moment by 6 and 8 % due to a volumetric increase as well as local changes in the coordination of Fe atoms (their magnetic moments are reduced for increasing number of Al neighbors but increased by the presence of Co). The APBs also enhanced the auxetic properties.