Switching of GeTe-Sb2Te3 multilayers by infrared femtosecond laser pulses — •Sonja Cremer1, Martin Ehrhardt1, Pierre Lorenz1, and Andriy Lotnyk1,21Leibniz Institute of Surface Engineering, Leipzig, Germany — 2Laboratory of Infrared Materials and Devices, Ningbo University, China

By phase change material multilayers (MLs) current drawbacks as resistance drift of Ge-Sb-Te thin films for neuromorphic computing may be tackled. This way MLs can help to unleash the full potential of the technologys advantageous characteristics like multilevel cell (MLC) operation. Switching is performed by electric or optical pulses, significantly changing the resistance and reflectivity of the thin film.

Here, we switched PLD grown 30 nm periodic GeTe-Sb2Te3-MLs using a 1030 nm laser with 260 fs pulse duration. The laser was part of an optical pump-probe setup to directly monitor reflectivity changes. Successful multiple switching was checked by light microscopy. Follow up SEM and TEM analysis were used to characterize the microstructure evolution. Switching between amorphous and fully crystalline state was found to go along with significant change in reflectivity (~20%). Besides, multilevel crystallization states with nonlinear reflectivity evolution were observed.

Thus, GeTe-Sb2Te3-MLs are a potential candidate for MLC operation with a fixed laser wavelength and pulse duration.

We acknowledge financial support by the DFG (No. 445693080) and thank Mrs. A. Mill for FIB preparation.

Keywords: phase change materials; multilayer; optical switching; multilevel storage; microstructure