Annealing effects on electrical properties of room-temperature deposited zinc oxynitride thin films — •Anna Reinhardt, Heiko Frenzel, Holger von Wenckstern, and Marius Grundmann — Universität Leipzig, Institut für Experimentelle Physik II, Semiconductor Physics Group

Amorphous oxide semiconductors have attracted much attention as channel material for thin-film transistors (TFT) due to their comparatively large electron mobility (>10 cm²/Vs) achieved already by low-temperature fabrication. In order to further increase channel mobilities while maintaining the stability of oxide-based TFTs the alloying of ZnO by nitrogen was suggested [1].

We have investigated the electrical properties of semiconducting zinc oxynitride (ZnO_xN_y) thin films depending on annealing temperature and doping. Therefore we conducted annealing experiments in air and N₂ atmosphere up to 400^∘C. The ZnO_xN_y thin films were deposited on glass substrates by reactive radio-frequency magnetron sputtering of a metallic zinc target at room-temperature. Electrical properties were examined using the four-probe van der Pauw technique. The as-deposited films show n-type semiconducting behaviour with carrier concentrations of 1×10¹⁷ − 3×10¹⁸ cm⁻³ and Hall mobilities ranging from 10 to 20 cm²/Vs. With increasing annealing temperature the resistivity decreases whereas the mobility increases. In addition, possible structural changes due to annealing were analyzed using x-ray diffraction.