Electrical and thermal transport properties of ZnGa2O4Johannes Boy1, Rüdiger Mitdank1, Zbigniew Galazka2, and •Saskia Fischer11Novel Materials Group, Humboldt-Univ. zu Berlin, Germany — 2Leibniz-Institute of Crystal Growth, Berlin, Germany

The first full experimental determination of the low-temperature electrical, thermo-electrical [1] and thermal properties [2] of novel highly pure single crystalline ZnGa2O4 is reported. The temperature-dependences of the charge carrier density, mobility, and Seebeck coefficient including phonon drag are discussed between 10 K and 310 K. The thermal conductivity and diffusivity were determined by the so-called 2ω-method. At room temperature the electrical conductivity is 286 S/cm, the mobility 55 cm2/Vs, the Seebeck coefficient 125 µ V/K and the thermal conductivity is 22.9 W/mK. For temperatures above 100 K the phonon transport is limited by phonon Umklapp scattering. At lower temperatures boundary scattering at lattice defects limits the thermal conductivity to 95 W/mK. Therefore, if the cause of boundary scattering is reduced or eliminated, the thermal conductivity of ZnGa2O4 may be increased at low temperatures.

[1] J. Boy, et al., AIP Advances 10, 055005 (2020) [2] J. Boy, et al., Materials Research Express 9, 065902 (2022).